南京磬海商贸有限公司

Technical data sheet for SILRES® BS 290 / Version: 1.5 / Date of last alteration: 11.04.2017 1 / Product description SILRES® BS 290 is a solventless silicone concentrate that is based on a mixture of silane and siloxane. SILRES® BS 290 is dilutable with organic solvents. Dilute solutions of SILRES® BS 290 in organic solvents serve as high-quality general-purpose water repellents for impregnating and priming mineral and highly alkaline substrates. Special features - good depth of penetration - high resistance to alkalis - tack-free drying - effective even on damp substrates - rapid development of water repellency After application to the mineral substrate, SILRES® BS 290 reacts with the atmospheric moisture or pore water in the substrate, thereby generating the active ingredient while liberating alcohol. The active ingredient greatly lowers the water absorbency of the substrate, which nevertheless retains a very high degree of water vapour permeability since neither pores nor capillaries are clogged. Application SILRES® BS 290 is suitable for imparting water repellency to absorbent, porous, mineral construction materials, e. g.: - brickwork - all kinds of concrete - aerated concrete - sand-lime brickwork - cement fiberboards - mineral plasters - mineral-based natural and artificial stone - mineral paints SILRES® BS 290 is also suitable as primer for exterior paints. SILRES® BS 290 is not suitable for rendering gypsum water repellent. Processing Flooding, preferably not under pressure, is the best technique for applying SILRES® BS 290, which is ready to use after dilution. Apply several coats, wet on wet, until the substrate is saturated. Generally, at leastwo applications suffice for all substrates. Do not leave long breaks between coats. Apply the next when the substrate has absorbed the previous one and is no longershiny (wet-on-wet working). The substrate must not have damp spots, i. e., it should look dry. The requisite quantity of SILRES® BS 290 depends on the adsorbency of the substrate. The amount of impregnating agent required for a substrate and the effectiveness of the impregnation should be determined on site by testing a small area of the material to be treated. Dilution The solvents best suited for diluting SILRES® BS 290 are aliphatic hydrocarbons (e. g. White Spirit 130/175)aromatic hydrocarbons (solvent naphtha, e. g. ShellsoA) or low-odor isoparaffin hydrocarbons (e. g. Isopar H). The solvent used should have a boiling range of 140-190°C and an evaporation number of 30-90. If the above-mentioned hydrocarbon solvents are used, SILRES® BS 290 should be diluted in a weight ratio of 1:11 to 1:15. Anhydrous alcohols, such as ethanol or 2-propanol, could also be used and are even indispensable whenever contact of the impregnating agent with solvent-sensitive materials (such as expanded polystyrene, bitumen, etc.) cannot be avoided. The alcohol must be completely anhydrous. If alcohol is used as a solvent, a dilution ratio of 1:12pbw is recommended. When impregnating slightly damp substrates, SILRES® BS 290 will give better results if diluted with hydrocarbons than with alcohol. Stir vigorously when adding the diluent to SILRES® B290. Since SILRES® BS 290 reacts with humidity, prolonged contact with air must be avoided. The containers must be hermetically sealed. Before applying SILRES® BS 290, be sure to cover SILRES® BS 290 MASONRY WATER REPELLENTSTechnical data sheet for SILRES® BS 290 / Version: 1.5 / Date of last alteration: 11.04.2017 2 / windows and other non-absorbent surfaces properly because the product cures so quickly that it wi